Исследование процесса тиснения на картонных складных коробках для косметической продукции по заказу ООО "Арт-Визаж Холдинг" 
Рис. 4.1. График зависимости остаточной деформации от температуры для SUGAR Lake Paper «Слоновая кость» 310 гр
Таблица 4.19
|
«Высоко-белый», Е0 = 0%, Н = 0 мкм
|
|
|
Т, С
|
Н внутр., мкм
|
Н внеш., мкм
|
|
|
1 сектор
|
2 сектор
|
3 сектор
|
4 сектор
|
1 сектор
|
2 сектор
|
3 сектор
|
4 сектор
|
|
|
180
|
96,0
|
40,0
|
35,0
|
84,0
|
76,0
|
42,0
|
39,0
|
67,0
|
|
|
123,0
|
47,0
|
30,0
|
91,0
|
67,0
|
47,0
|
34,0
|
55,0
|
|
|
94,0
|
46,0
|
39,0
|
79,0
|
83,0
|
47,0
|
36,0
|
68,0
|
|
|
среднее
|
104,3
|
44,3
|
34,7
|
84,7
|
75,3
|
45,3
|
36,3
|
63,3
|
|
|
160
|
85,0
|
29,0
|
23,0
|
82,0
|
48,0
|
36,0
|
31,0
|
52,0
|
|
|
73,0
|
29,0
|
21,0
|
77,0
|
58,0
|
33,0
|
31,0
|
53,0
|
|
|
71,0
|
34,0
|
25,0
|
77,0
|
51,0
|
46,0
|
31,0
|
57,0
|
|
|
среднее
|
76,3
|
30,7
|
23,0
|
78,7
|
52,3
|
38,3
|
31,0
|
54,0
|
|
|
140
|
37,0
|
10,0
|
|
69,0
|
44,0
|
25,0
|
23,0
|
47,0
|
|
|
33,0
|
8,0
|
|
57,0
|
43,0
|
30,0
|
27,0
|
41,0
|
|
|
37,0
|
23,0
|
|
67,0
|
40,0
|
25,0
|
27,0
|
48,0
|
|
|
среднее
|
35,7
|
13,7
|
|
64,3
|
42,3
|
26,7
|
25,7
|
45,3
|
|
|
120
|
27,0
|
|
|
38,0
|
33,0
|
|
|
25,0
|
|
|
23,0
|
|
|
31,0
|
40,0
|
|
|
25,0
|
|
|
27,0
|
|
|
43,0
|
37,0
|
|
|
28,0
|
|
|
среднее
|
25,7
|
|
|
37,3
|
36,7
|
|
|
26,0
|
|
|
100
|
|
|
|
|
25,0
|
|
|
17,0
|
|
|
|
|
|
|
20,0
|
|
|
20,0
|
|
|
|
|
|
|
33,0
|
|
|
31,0
|
|
|
среднее
|
|
|
|
|
26,0
|
|
|
22,7
|
|
|
Рис. 4.2. График зависимости остаточной деформации от температуры для SUGAR Lake Paper «Высоко-белый» 310 гр
Таблица 4.20
|
«Бронза», Е5 = 0,68%, Н = 10,57 мкм
|
|
|
Т, С
|
Н внутр., мкм
|
Н внеш., мкм
|
|
|
1 сектор
|
2 сектор
|
3 сектор
|
4 сектор
|
1 сектор
|
2 сектор
|
3 сектор
|
4 сектор
|
|
|
180
|
248,0
|
118,0
|
75,0
|
254,0
|
287,0
|
123,0
|
111,0
|
262,0
|
|
|
201,0
|
120,0
|
77,0
|
266,0
|
316,0
|
156,0
|
118,0
|
277,0
|
|
|
среднее
|
224,5
|
119,0
|
76,0
|
260,0
|
301,5
|
139,5
|
114,5
|
269,5
|
|
|
160
|
122,0
|
76,0
|
82,0
|
108,0
|
194,0
|
103,0
|
86,0
|
155,0
|
|
|
138,0
|
66,0
|
76,0
|
101,0
|
176,0
|
138,0
|
96,0
|
157,0
|
|
|
среднее
|
130,0
|
71,0
|
79,0
|
104,5
|
185,0
|
120,5
|
91,0
|
156,0
|
|
|
140
|
163,0
|
64,0
|
59,0
|
105,0
|
181,0
|
117,0
|
80,0
|
161,0
|
|
|
88,0
|
54,0
|
37,0
|
100,0
|
172,0
|
94,0
|
67,0
|
144,0
|
|
|
среднее
|
125,5
|
59,0
|
48,0
|
102,5
|
176,5
|
105,5
|
73,5
|
152,5
|
|
|
120
|
120,0
|
57,0
|
46,0
|
92,0
|
150,0
|
100,0
|
71,0
|
146,0
|
|
|
90,0
|
|
|
81,0
|
150,0
|
94,0
|
69,0
|
139,0
|
|
|
среднее
|
105,0
|
57,0
|
46,0
|
86,5
|
150,0
|
97,0
|
70,0
|
142,5
|
|
|
Рис. 4.3. График зависимости остаточной деформации от температуры для РЕГЕНТ Маджестик «Бронза» (двухсторонний) 250 гр
Таблица 4.21
|
«Золото», Е0 = 0%, Н = =0 мкм
|
|
|
Т, С
|
Н внутр., мкм
|
Н внеш., мкм
|
|
|
1 сектор
|
2 сектор
|
3 сектор
|
4 сектор
|
1 сектор
|
2 сектор
|
3 сектор
|
4 сектор
|
|
|
180
|
|
|
|
71,0
|
63,0
|
48,0
|
27,0
|
75,0
|
|
|
|
|
|
65,0
|
68,0
|
48,0
|
35,0
|
90,0
|
|
|
|
|
|
|
65,0
|
37,0
|
37,0
|
94,0
|
|
|
среднее
|
|
|
|
68,0
|
65,3
|
44,3
|
33,0
|
86,3
|
|
|
160
|
50,0
|
28,0
|
20,0
|
63,0
|
85,0
|
35,0
|
24,0
|
78,0
|
|
|
53,0
|
|
21,0
|
63,0
|
84,0
|
31,0
|
28,0
|
81,0
|
|
|
48,0
|
|
22,0
|
65,0
|
75,0
|
29,0
|
27,0
|
78,0
|
|
|
среднее
|
50,3
|
28,0
|
21,0
|
63,7
|
81,3
|
31,7
|
26,3
|
79,0
|
|
|
140
|
31,0
|
|
|
23,0
|
67,0
|
17,0
|
10,0
|
42,0
|
|
|
30,0
|
|
|
38,0
|
66,0
|
19,0
|
15,0
|
39,0
|
|
|
30,0
|
|
|
41,0
|
62,0
|
20,0
|
14,0
|
64,0
|
|
|
среднее
|
30,3
|
|
|
34,0
|
65,0
|
18,7
|
13,0
|
48,3
|
|
|
120
|
|
|
|
18,0
|
34,0
|
15,0
|
|
33,0
|
|
|
|
|
|
16,0
|
32,0
|
12,0
|
|
42,0
|
|
|
|
|
|
13,0
|
29,0
|
14,0
|
|
34,0
|
|
|
среднее
|
|
|
|
15,7
|
31,7
|
13,7
|
|
36,3
|
|
|
100
|
|
|
|
|
26,0
|
|
|
17,0
|
|
|
|
|
|
|
27,0
|
|
|
15,0
|
|
|
|
|
|
|
28,0
|
|
|
16,0
|
|
|
среднее
|
|
|
|
|
27,0
|
|
|
16,0
|
|
|